I-TK-APMI-Ferro-Chromium-I-Aluminium Alloy

Le mveliso ithatha i-master alloy ecocekileyo njengezinto eziluhlaza, kwaye isetyenziswai-powder metallurgyubuchwepheshe

ukwenza ii-ingots ze-alloy, kwaye yenziwa ngokucubungula okukhethekileyo okubandayo nobushushu kunye nobushushu

inkqubo yonyango. Le mveliso ineenzuzo zokumelana ne-oxidation enamandla, ilungile

ukumelana nokugqwala kubushushu obuphezulu, ukurhubuluza okuncinci kwezinto ze-electrothermal, inkonzo ende

ubomi kubushushu obuphezulu kunye notshintsho oluncinci lokumelana. Ifanelekile kubushushu obuphezulu be-1420 C,

uxinano olukhulu lwamandla, umoya okonakalisayo, umoya wekhabhoni kunye nezinye iindawo zokusebenza.

Ingasetyenziswa kwii-oven ze-ceramic, kwii-oven zonyango lobushushu obuphezulu, kwii-oven zelabhoratri,

ii-oven ze-elektroniki zoshishino kunye nee-oven ezisasazwayo.

(IsiNgesi)Ubungakanani%）ulwakhiwo oluphambili

Iipropati eziphambili zoomatshini

Amandla okuThamba kwiqondo lobushushu legumbi: 650-750MPa

Izinga lobude: 15-25%

ubunzima: HV220-260

Amandla okuThamba kwi-1000℃ Ubushushu obuyi-22-27MPa

Ukuqina kobushushu obuphezulu kwi-1000 Temperature kunye ne-6MPa ≥100h

Iimpawu eziphambili zomzimba

uxinano 7.1g/cm3

ukumelana 1.45×10-6 Ω.m

Ukumelana nobushushu obuqhelekileyo(IsiNgesi)Ct）

I-avareji ye-coefficient yokwandisa emgceni()

Ubushushu obuphezulu bokusebenza obuqhubekayo yi-1400℃

Ubomi obukhawulezayo

 Uvavanyo ngokwendlela eqhelekileyo ye-GB/T13300-91