Ukuveliswa kunye neFektri yeCopper Nickel yaseTshayina iConstantan Flat Wire 6j40 Ribbon 0.4*2mm

I-Constantan Flat Wire Copper Nickel Alloy 6j40 Ribbon 0.4*2mm Umfanekiso obonisiweyo

I-Constantan Flat Wire Copper Nickel Alloy 6j40 Iribhoni 0.4*2mm

Inkcazo emfutshane:

I-Constantan Flat Wire Copper Nickel Alloy 6j11 Iribhoni 0.4*2mm

Ukuxhathisa ( 200C μ Ω. m): 0.1
Ubushushu obuphezulu bokusebenza (0C):200
Amandla okuThamba (i-Mpa): ≥ 250
Indawo yokunyibilika (0C): 1095
Ubuninzi (g/cm3):8.9
I-TCR x10-6/ 0C (20~600 0C): < 100

Isatifikethi:I-ISO 9001

Ubungakanani:Yenzelwe wena

Igama lemveliso :I-Copper Nickel Alloy 6j11

isicelo:imboni

izinto:ingxubevange

uphawu:ukumelana okuphezulu

umsebenzi:uzinzo oluhle kwimo

ubunzima:isekelwe

ubukhulu:njengemfuneko yomthengi

umbala:ntsundu

imilo:ucingo

I-MOQ:20kg

Thumela i-imeyile kuthi

Iinkcukacha zeMveliso

FAQ

Iithegi zeMveliso

I-Constantan Flat Wire Copper Nickel Alloy entsha 6j11 Ribbon 0.4*2mm

Uphawu	Ukumelana (200C μΩ.m)	Ubushushu obuphezulu bokusebenza (0C)	Amandla okuThamba (i-Mpa)	Iqondo lokunyibilika (0C)	Ubuninzi (g/cm3)	I-TCR x10-6/ 0C (20~600 0C)	EMF vs Cu (μ V/ 0C) (0~100 0C)
Amagama e-alloy
I-NC003 (CuNi1)	0.1	200	≥ 250	1095	8.9	< 100	-12

Iipropati Zomzimba	I-Metric	Izimvo
Uxinano	8.94 g/cc
Iipropati zoomatshini	I-Metric	Izimvo
Amandla okuThamba, Okona kulungileyo	262 – 531 MPa
Amandla okuThamba, ukuKhuthaza	276 – 524 MPa	Kuxhomekeke kumsindo
Ukwandiswa ngexesha lokuphumla	46.0%	kwi-50.8 mm.
Imodulus ye-Elasticity	115 GPa
Umlinganiselo wePoissons	0.310	Kubalwe
Ukungakwazi ukusebenza	20%	I-UNS C36000 (ithusi elisikayo ngokukhululekileyo) = 100%
I-Shear Modulus	44.0 GPa
Iipropati zoMbane	I-Metric	Izimvo
Ukumelana nombane	0.0000120 ohm-cm @Ubushushu 20.0 ° C
Iipropati zoBushushu	I-Metric	Izimvo
I-CTE, ethe ngqo	17.5 µ m/m-° C @Ubushushu 20.0 – 300 ° C
Umthamo othile wobushushu	0.380 J/g-° C
Ukuqhuba kweThermal	64.0 W/mK @Ubushushu 20.0 ° C
Indawo yokunyibilika	< = 1125 ° C	I-Liquidus
I-Liquidus	1125 ° C
Iipropati zokucubungula	I-Metric	Izimvo
Ubushushu bokuNgcwaba	565 – 815 ° C
Ubushushu obusebenza ngokushushu	815 – 950 ° C
Iipropati zeZinto eziQokelelweyo	I-Metric	Izimvo
Ubhedu, Cu	> = 91.2 %
Intsimbi, iFe	1.30 – 1.70 %
Inkokeli, iPb	< = 0.050 %
IManganese, Mn	0.30 – 0.80 %
Nickel, Ni	4.80 – 6.20 %
I-Zinc, i-Zn	< = 1.0 %

Umxholo weekhemikhali zeCuNi44, %

Ni	Mn	Fe	Si	Cu	Okunye	Isikhokelo seROHS
						Cd	Pb	Hg	Cr
44	1%	0.5	-	I-Bal	-	ND	ND	ND	ND

Iipropati zoomatshini

Ubushushu beNkonzo eQhubekayo obuphezulu	400ºC
Ukuqina kwakhona kwi-20ºC	0.49±5%ohm mm2/m
Uxinano	8.9 g/cm3
Ukuqhuba kweThermal	-6(Ubuninzi)
Indawo yokunyibilika	1280ºC
Amandla okuThamba, i-N/mm2 eqhotyoshelweyo, ethambileyo	340~535 Mpa
Amandla okuThamba, i-N/mm3 eQokelelweyo ebandayo	680~1070 Mpa
Ukwandiswa (i-anneal)	25% (Ubuncinane)
Ukwandiswa (okuqengqelekayo okubandayo)	≥Mncinci)2% (Mncinci)
I-EMF vs i-Cu, μV/ºC (0~100ºC)	-43
Ulwakhiwo lweMicrographic	i-austenite
Ipropati yeMagnetic	Hayi