I-Alkrothal 14 i-ferchromicumUmium allous Allowy (Fecrolil Allow)
I-Alkrothal 14 (Ukuchasana nokufudumeza i-wire kunye nokuxhathisa i-Alkrothal 14 yi-Ferchrothal Alkromiumonuum alloy (iFecrolic) ngokuchasene ne-11 ° C). I-Alkrothal 14 isetyenziselwa i-wire yokunganyangeki yombane kwizicelo ezinje ngeentambo zokufudumeza.
Ukwakhiwa kweekhemikhali
| C% | I-7% | Mn% | Cr% | Al% | Fe. | |||||||
| ukwakhiwa okuthile | 4.3 | I-bal | ||||||||||
| Imiz | - | 14.0 | ||||||||||
| Max | I-0.08 | 0.7 | 0.5 | 16.0 |
Iipropathi zoomatshini
| Ubungakanani bocingo | Unikeze Amandla | Tensile strength | I-elongwation | Ubunzima |
| Ø | Rp0.2 | Rm | A | |
| mm | Mpa | Mpa | % | Hv |
| 1.0 | 455 | I-630 | 22 | I-220 |
| 4.0 | 445 | I-600 | 22 | I-220 |
| 6.0 | 425 | I-580 | 23 | I-220 |
Imodyuli yoMncinci
| iqondo lobushushu ° c | 20 | I-100 | 200 | I-400 | I-600 | I-800 | I-1000 |
| I-GPA | I-220 | I-210 | 205 | I-190 | I-170 | I-150 | I-130 |
Iipropathi zoomatshini kwiqondo lobushushu eliphakamileyo
| Iqondo lobushushu ° c | I-900 |
| Mpa | 30 |
Ixabiso lokugqibela le-Ginfort Esform 6.2 x 10 / min
Amandla e-cree-1% ye-elongwation kwi-1000 h
| Iqondo lobushushu ° c | I-800 | I-1000 |
| Mpa | 1.2 | 0.5 |
Iipropathi zomzimba
| Ukuxinana g / cm3 | 7.28 |
| Ukunganyange kombane kwi-20 ° C ω / m | 1.25 |
| Umyinge wePoisson | I-0.30 |
I-HOPT EBALASELEYO YOKUGQIBELA
| Iqondo lobushushu ° c | I-100 | 200 | I-300 | I-400 | I-500 | I-600 | I-700 | I-800 | I-900 | I-1000 | I-1100 |
| Ct | 1.00 | 1.02 | 1.03 | 1.04 | 1.05 | 1.08 | 1.09 | 1.10 | 1.11 | 1.11 | 1.12 |
Ukusebenza kolwando lwe-shirmal
| Iqondo lobushushu ° c | Ukwanda kwe-therm 106/ K |
| 20 - 250 | 11 |
| 20 - 500 | 12 |
| 20 - 750 | 14 |
| I-20-1000 | 15 |
Ukuqhubela phambili kwe-thermal
| Iqondo lobushushu ° c | 20 |
| W / m k | 16 |
Umthamo othile wobushushu
| Iqondo lobushushu ° c | 20 | 200 | I-400 | I-600 | I-800 | I-1000 |
| kj kg-1K-1 | I-0.46 | 0.63 | 0.72 | 1.00 | I-0.80 | 0.73 |